white rustic tile
white rustic tiles best saller thickness:9.5-10mm water absorption:0.3-0.5%
rustic tiles
| Test Item | Enterprise Standar | ISO | EN Standar | GB Standar | ||||
| chemistry rust Resistance | ISO 13006:GA EN 178:A GB/Tz4100:GHA | Not limite to GB level | The lowest B level | Determine the level between the supplier and the consumer | ||||
| Edge straight | ±0.2 | ±0.4 | ±0.5 | ±0.4 | ||||
| Right angle degree | ±0.25 | ±0.4 | ±0.4 | ±0.4 | ||||
| Water absorption | E≤0.5% 6<E≤8% | E≤0.5% 6<E≤10% | E≤0.5% 6<E≤10% | E≤0.5% 6<E≤10% | ||||
| Thickness | ±3.0 | ±5.0 | ±5.0 | ±5.0 | ||||
| Length | ±0.3 | ±0.6 | ±0.6 | ±0.6 | ||||
| Width | ±0.2 | ±0.4 | ±0.4 | ±0.4 | ||||
| Edge bending degree | ±0.3 | ±0.4 | ±0.5 | ±0.4 | ||||
| Breakage modulus | ≥22Mpa | ≥18Mpa | ≥18Mpa | ≥18Mpa | ||||
| Central bending degree | ±0.3 | ±0.4 | ±0.4 | ±0.4 | ||||
| Heat&shake resistance | ‹15°C-145°C›nacrack occurs after 10heat cycles | ‹15°C-145°C›nacrack occurs after 10heat cycles | ‹15°C-145°C›nacrack occurs after 10heat cycles | ‹15°C-145°C›nacrack occurs after 10heat cycles | ||||
| Chapresistance | no crack occurs under 500Kpa pressure 1time /2hours | no crack occurs under 500Kpa pressure 1time /2hours | no crack occurs under 500Kpa pressure 1time /2hours | no crack occurs under 500Kpa pressure 1time /2hours | ||||
| Wearable | Determined by both the supplier and consumer | Determined by both the supplier and consumer | Determined by both the supplier and consumer | no crack occurs under 500Kpa pressure 1time /2hours |
white rustic tile