Hot Rolled Steel Coil
Hot rolled sheet is the most important varieties of steel in sheet metal, widely used in containers, vehicles, railway ect.
Prime Hot Rolled Steel Coil
Steel Grade: SS400/Q235B/ASTM A36/S235JR/S275JR/Q345B/Q345C
Thickness:1.5mm-20mm
Width:1200mm-2000mm
Packing:Mill's stardard export packing
Shipment:Bulk vessel within one month after received L/C or T/T
Chemical composition | ||||||
Grade | Chemical composition(Melting analysis)% | |||||
C | Mn | S | P | Si | Als | |
SPHC | ≤0.15 | ≤0.60 | ≤0.025 | ≤0.030 | ≤0.050 | ≥0.010 |
SPHD | ≤0.10 | ≤0.50 | ≤0.025 | ≤0.025 | ≤0.030 | ≥0.015 |
SPHE | ≤0.08 | ≤0.50 | ≤0.020 | ≤0.025 | ≤0.030 | ≥0.015 |
DD11(StW22) | ≤0.12 | ≤0.60 | ≤0.025 | ≤0.025 | ≤0.030 | ≥0.010 |
DD12(StW23) | ≤0.10 | ≤0.45 | ≤0.020 | ≤0.025 | ≤0.030 | ≥0.015 |
DD13(StW24) | ≤0.08 | ≤0.40 | ≤0.015 | ≤0.020 | ≤0.030 | ≥0.015 |
Mechanical properties | |||||||||
Grade | Tensile test | 180° bending test | |||||||
Tensile strength(Rm/Mpa) | Elongation(A%) as below thickness(mm) | ||||||||
Less1.6 | 1.6~2.0 | 2.0~2.5 | 2.5~3.2 | 3.2~4.0 | ≥4.0 | less3.2 | ≥3.2 | ||
SPHC | ≥270 | ≥27 | ≥29 | ≥30 | ≥31 | ≥32 | ≥32 | Oa | 1a |
SPHD | ≥270 | ≥30 | ≥32 | ≥33 | ≥35 | ≥37 | ≥39 | 0a | |
SPHE | ≥270 | ≥31 | ≥33 | ≥35 | ≥37 | ≥39 | ≥41 | 0a |
Grade | Tensile test | ||||||
Yield Strength(Rel/Mpa) as below thickness | Tensile strength(Rm/Mpa) | Elongation(A%) as below thickness(mm) | 180°bending test, Apex diameter | ||||
Lo=80mm b=20mm | Lo=5.65\Rso | ||||||
2 | 2.0-8.0 | 1.5-2.0 | 2.0-3.0 | 3.0-8.0 | |||
DD11(StW22) | 170-360 | 170-340 | ≤440 | ≥23 | ≥24 | ≥28 | 2a |
DD12(StW23) | 170-340 | 170-320 | ≤420 | ≥25 | ≥26 | ≥30 | 0a |
DD13(StW24) | 170-330 | 170-310 | ≤400 | ≥28 | ≥29 | ≥33 | 0a |
Hot Rolled Steel Coil