1.Content:MgO80%min C10%min 2.High temperature liquidity 247min(1000degrees) 3.MOQ:20MT 4.As customer's special demands
Converter Self-flow Patching Material
Advantage
1. Well spread, even coverage on the surface of molten iron and steel
2. The content is steady, it has good fluxing capacity, while using won’t cause crust or erode the ladle wall, so it is easy to clean the ladle.
3. Appropriate alkalinity, it won’t pollute the molten iron and steel, meanwhile it can absorb other inclusion
Certificate
1.ISO approval.
2.Certified as "qualified & reliable" manufacturer by CIQ.
3.Mill's test reported as each 1MT/ p.p bag by CIQ.
Production lead time &shippment
1.Prompt producing after order,with 35 tons capability a day.
2.Shipment with 5 working days after production.(ship to Korea&Japan about 2 days,ship to Brazil(North America) about 35 days)
Specification
| Item | Composition(%) | Gravity Density(g/cm3) | Rupture Strengh(MPa) | Porosity(%) | High Temperature Liquidity (mm) | ||||
| MgO | C | 1000°C | 1500°Cx3h | 1000°C | 1500°Cx3h | 1000°C | 1500°Cx3h | 1000°C | |
| Coverter Self-flow Patching | ≥ 80.0 | ≥ 10.0 | ≥ 2.4 | ≥ 2.3 | ≥12.0 | ≥ 7.8 | ≤ 15.0 | ≤ 15.5 | ≥247 |
Good quality refractory Converter Self-flow Patching Material