CA50-N is early strength aluminate binder, whose 6 hours compressive strength can reach 20-30MPa
Aluminate cement CA50-N
(1)Chemical Analysis
Al2O3: 50.0% min
SiO2: 7.0% Max.
Fe2O3: 2.5% Max.
CaO: 34.5% min
(2) Physical Properties
initial set time: 0:30mins min
final set time: 6h:00 max
Specific surface area: 300m2/kg min.
flexural strength
6hours 4.0Mpa min.
1 day 6.0Mpa min.
3 days 7.0Mpa min.
Compressive strength
6hours 30.0Mpa min
1 day 50.0Mpa min.
3 day 60.0Mpa min
Test Methd:GB201-2000
CA50-N is early strength aluminate binder, tested according to GB201-2000, whose 6 hours compressive strength can reach 20-30Mpa . It can be de-molded within one day when producing mid-low cement castable.
Early Strength Calcium Aluminate Cement CA50-N