Environmentally friendly PVC cable compound
1.Good plasticization 2.Uniform color 3.No significant impurities 4.Environmently friendly
Environmentally friendly PVC cable compounds are made mainly from PVC resin together with various additives such as non-toxic,pollution-free,multi-functional plasticizer,stabillzer,through mixing,plasticizing and granulation.
1.Application
| TYPE | PRODUCT NAME | The max allowable operating temperature of the conductive core | Application |
| J-70 | Environmently friendly PVC insulating compound | 70°C | Used for instrument and communication cable which working voltage less than 0.6/1KV |
| J-90 | Environmently friendly PVC insulating compound | 90°C | Used for hot resistant wires and cables which working voltage less than 450/750V |
| J-105 | Environmently friendly PVC insulating compound | 105°C | Used for wires and cables which working voltage less than 26/35KV |
| H-70 | Environmently friendly PVC jacket compound | 70°C | Used for wires and cables which working voltage less than 26/35KV |
| H-90 | Environmently friendly PVC jacket compound | 90°C | Used for wires and cables which working voltage less than 26/35KV |
| HTM-70 | 70°C transparent and non-toxic VC jacket compound | 70°C | Used for speaker cables and other wire and cables which requiring transparent |
| HTM-90 | 90°C transparent and non-toxic VC jacket compound | 90°C | Used for speaker cables and other wire and cables which requiring transparent |
2.Performance indicator
| NO. | TYPE | HTM-70 | HTM-90 | J-70 | J-90 | J-105 | H-70 | H-90 | |
| 1 | Tensile strength MPa ≥ | 12.5 | 15 | 15 | 16 | 16 | 15 | 16 | |
| 2 | Tensile strain at break ≥ | 180 | 180 | 150 | 150 | 150 | 180 | 180 | |
| 3 | Thermal deformation ≤ | 50 | 40 | 40 | 30 | 30 | 50 | 40 | |
| 4 | Impact brittleness temperature °C | -25 | -20 | -15 | -15 | -15 | -25 | -20 | |
| 5 | Volume resistance at 20°C Ω.m ≥ | 1.0x108 | 1.0x109 | 1.0x1012 | 1.0x1012 | 1.0x1012 | 1.0x108 | 1.0x109 | |
| 6 | Volume resistance rate at operation temperature | Test temperature °C | 70±1 | 95±1 | 95±1 | ||||
| Volume resistivity Ω.m ≥ | 1.0x109 | 5.0x108 | 5.0x108 | ||||||
| 7 | Dielectric strength MV/m ≥ | 18 | 18 | 20 | 20 | 20 | 18 | 18 | |
| 8 | Thermal stable time 200°C min | 50 | 80 | 90 | 180 | 80 | 50 | 80 | |
| 9 | Properties after thermal aging | Test temperature °C | 80±2 | 100±2 | 100±2 | 135±2 | 135±2 | 100±2 | 100±2 |
| Test time h | 168 | 240 | 168 | 240 | 168 | 168 | 240 | ||
| Tensile strength after aging ≥ | 12.5 | 15 | 15 | 16 | 16 | 15 | 16 | ||
| The max change of elongation | ±20 | ±20 | ±20 | ±20 | ±20 | ±20 | ±20 | ||
| Tensile strain after aging ≥ | 180 | 180 | 150 | 150 | 150 | 180 | 180 | ||
| The max change of elongation | ±20 | ±20 | ±20 | ±20 | ±20 | ±20 | ±20 | ||
| Quality loss after thermal aging g/m2 ≤ | 20 | 15 | 20 | 20 | 20 | 23 | 15 | ||
| 10 | Sb ≤mg/kg | 60 | 60 | 60 | 60 | 60 | |||
| 11 | As ≤mg/kg | 25 | 25 | 25 | 25 | 25 | |||
| 12 | Ba ≤mg/kg | 500 | 500 | 500 | 500 | 500 | |||
| 13 | Cd ≤mg/kg | 50 | 50 | 50 | 50 | 50 | |||
| 14 | Cr ≤mg/kg | 25 | 25 | 25 | 25 | 25 | |||
| 15 | Pb ≤mg/kg | 90 | 90 | 90 | 90 | 90 | |||
| 16 | Hg ≤mg/kg | 25 | 25 | 25 | 25 | 25 | |||
| 17 | Se ≤mg/kg | 60 | 60 | 60 | 60 | 60 | |||
Workshop
Product
Raw material
Details of the product
Environmentally friendly PVC cable compound