1.Flame Retardant PP Granules 2.UL94 V0 Flame retardance 3.ISO9001, ISO14001,ISO/TS16949 4.RoSH Test 5.Made of new material
Flame Retardant PP Plastic Granules (P-R)
(Flame Retardant Plastic )
Advantages:
1. Flame Retardant UL94 V0
2. High heat resistance
3. High toughness
4. Totally made of new Material
Application: Electrical frame; Switch parts; Appliance parts; Electronic components
Specification:
Properties | ASTM | Test Condition | Unit | Specifications | ||
PP-R-01 | PP-R-02 | PP-R-03 | ||||
Physical Properties | ||||||
Density | D-792 | 23°C | g/cm3 | 1.20 | 1.28 | 1.35 |
Melt Flow Index | D-1238 | 230°C/2.16Kg | g/10min | 0.5-10 | 0.5-10 | 0.5-10 |
Mold Shrinkage | D-955 | 23°C | % | 0.9-1.2 | 0.9-1.2 | 0.9-1.2 |
Mechanical Properties | ||||||
Tensile Strength | D-638 | 10mm/min | MPa | 26 | 28 | 30 |
Elongation at Break | D-638 | 10mm/min | % | 50 | 50 | 50 |
Flexural Strength | D-790 | 2mm/min | MPa | 35 | 38 | 45 |
Flexural Modulus | D-790 | 2mm/min | MPa | 1300 | 1600 | 1800 |
IZOD Impact Strength notched | D-256 | 3.2mm,23°C | KJ/m2 | 12.0 | 11.0 | 10.0 |
Thermal Properties | ||||||
Heat Distortion Temperature | D-648 | 0.45MPa,6.4mm | °C | 115 | 120 | 125 |
Vicat Softening Temperature | D1525 | 1Kg, 50°C/h | °C | 140 | 145 | 150 |
Others | ||||||
Flammability | UL-94 | 1.6mm | — | V0 | V0 | V0 |
Filler Content | — | — | % | — | — | — |
Characteristics | Environment friendly Flame retardant | |||||
[1] Dyes materials characters will be different from above value.
[2] Typical values are for average laboratory data. It is only suit for utilizing reference, not on products standard.
Package: Coextruded Paper Bag, 25.0kgs/bag
( Flame Retardant Plastic ) High Flame Retardanct PP Plastic Granule