White Micro Fine Power PVC Paste Resin (Emulsion Grade) 1.LG 1302/1202,P440/P450 2.for leather,flooring 3.technic support
White Micro Fine Power PVC Paste Resin (Emulsion Grade)
Product : PVC Paste Resin (Emulsion PVC Resin)
Formula : (C2H3Cl)n H.S.CODE : 3904101000
CAS No. : 9002-86-2
1.Characteristic:
Paste PVC resin is a homopolymer of PVC which is made by emulsion polymerization,it can be used for coating cloth, rotary forming, macerating, spraying and foaming after mixed with plasticizer and other addition agent. It is a light white and micro fine powder .
2.Specification:
| Specs | Type Index | ||||
| XBRE-1 | XBRE-2 | XBRE-3 | XBRE-4 | ||
| Viscosity (Ml/G) | 160 Min | 155-165 | 155-145 | 140-150 | |
| K Value | 78.0 Min | 75.0-79.0 | 75.0-79.0 | 73.5-76.0 | |
| Polymerization Degree | 1850 Min | 1750-1950 | 1550-1750 | 1475-1650 | |
| B-type Viscosity 30° C mpa. s | 4.0 Max | 3.0-5.0 | 5.0-7.0 | 4.0-7.0 | |
| Volatile % ≤ | 0.4 | 0.4 | 0.4 | 0.4 | |
| Bulk density, g/cm 3 | 0.3-0.45 | ||||
| Remain % mg/kg | 0.25mm Sieve ≤ | 0.01 | 0.01 | 0.01 | 0.01 |
| 0.063mm Sieve ≤ | 0.1 | 0.1 | 0.1 | 0.1 | |
| DOP: resin (portion) | 60: 100 | 100: 100 | 60: 100 | 100: 100 | |
| Apparent | White micro powder | ||||
3. Application:
XBRE-1: non foaming artificial leather bottom,surface of artificial leather and floor leather,canvas,maceration forming(gloves,boots),rotary forming(toy),hollow forming and rubber, bottle caps.XBRE-2: artificial leather foaming layer,bottle cap(pad),steel plate coating,eraser,formulation with high plasticizer content,maceration forming.XBRE-3:
Mainly used for non-foaming or micro-foaming artificial leather, also be used in coating, glass fiber, macerating, textile printing and general products
XBRE 4: canvas, soft pipe, fabric tablecloth, artificial leather foaming layer
4.Packing:
25kg/bag or as per your requirement.
5.Store andtransport:
Prevent from rain,snow,humid,sunshine,throwing and other mechanical damage.
White Micro Fine Powder Paste PVC Resin (Emulsion Grade)