1. Low density, good handle and surface, good dimension stability 2.Soft insole and demold fast 3.Hydrolysis resistance
Characteristic: Low density, good handle and surface, good dimension stability | ||||||||||||||||
Application: Insole | ||||||||||||||||
Typical properties of PU matrix
| ||||||||||||||||
Materials preheat A-1001A: preheated at 50~60°C for 8~12hours B-5301: preheated at 60~70°C for 18~22 hours | ||||||||||||||||
Typical processing parameters & Reaction parameter
The adding content of C-2 should be 380g±20g/18kg The adding content of water should be 0~90g/18kg according to the reality The adding content of water should be 0~600g/18kg according to the reality | ||||||||||||||||
Physical properties
| ||||||||||||||||
Demold time may be prolonged with the increase of sole thickness | ||||||||||||||||
These physical data are acquired by testing a sample of 6mm thick. | ||||||||||||||||
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for Physical properties, please contact us. |
Polyol and Isocynate resins for insole