heat shrinkable tube Feature: 1.Material:polyolefin 2.shrink temperature: 90 3.Temperature Renge :-55-125 heat shrinkable tube:Instr: shrink temperature: 90oC
Temperature Renge :-55-125
Radial Shrinking Ratio : ≥50%
longitudinal shrinking ratio : ≤5%
Tensile Strength : ≥14Mpa
Aging : 158.0±1.0°Lays aside for 7 days 7Days Air Cren at158.0±1.0 Through
134.0±1.0°Lays aside for 60 days 60Days Air Cren at134.0±1.0
Tensile Stength after Aging : ≥10Mpa
Elongation after Aging : ≥200%
Volume Resistivity :≥10Ω·cm
Dielectric strength :≥25KV/mm
Flammability : VW-1
| Product specification | Before the contraction(mm) | After the contraction(mm) | Standard packing | ||
| Minimum inside diameter | Wall thickness | Maximum inside diameter | Wall thickness | ||
| φ0.8 | 1.00±0.30 | 0.18 | 0.4 | 0.33 | 200 |
| φ1.0 | 1.50±0.30 | 0.18 | 0.5 | 0.33 | 200 |
| φ1.5 | 2.00±0.30 | 0.18 | 0.75 | 0.36 | 200 |
| φ2.0 | 2.50±0.30 | 0.25 | 1 | 0.43 | 200 |
| φ2.5 | 3.00±0.30 | 0.25 | 1.25 | 0.43 | 200 |
| φ3.0 | 3.50±0.30 | 0.25 | 1.5 | 0.43 | 200 |
| φ3.5 | 4.00±0.30 | 0.25 | 1.75 | 0.43 | 200 |
| φ4.0 | 4.50±0.30 | 0.25 | 2 | 0.43 | 200 |
| φ5.0 | 5.50±0.30 | 0.25 | 2.5 | 0.43 | 100 |
| φ6.0 | 6.50±0.30 | 0.25 | 3 | 0.56 | 100 |
| φ7.0 | 7.50±0.30 | 0.3 | 3.5 | 0.56 | 100 |
| φ8.0 | 8.50±0.30 | 0.3 | 4 | 0.56 | 100 |
| φ9.0 | 9.50±0.30 | 0.3 | 4.5 | 0.56 | 100 |
| φ10.0 | 10.50±0.50 | 0.3 | 5 | 0.56 | 100 |
| φ11.0 | 11.50±.50 | 0.3 | 5.5 | 0.56 | 100 |
| φ12.0 | 12.50±0.50 | 0.3 | 6 | 0.56 | 100 |
| φ13.0 | 13.50±0.50 | 0.35 | 6.5 | 0.69 | 100 |
| φ14.0 | 14.50±0.50 | 0.35 | 7 | 0.69 | 100 |
| φ15.0 | 15.50±0.60 | 0.35 | 7.5 | 0.69 | 100 |
| φ16.0 | 16.50±0.60 | 0.35 | 8 | 0.69 | 100 |
| φ17.0 | 19.00±0.60 | 0.4 | 9 | 0.76 | 100 |
| φ18.0 | 21.00±0.60 | 0.4 | 10 | 0.76 | 100 |
| φ20.0 | 23.00±0.70 | 0.45 | 11 | 0.89 | 100 |
| φ22.0 | 26.00±0.70 | 0.45 | 12.5 | 0.89 | 50 |
| φ28.0 | 29.50±0.70 | 0.45 | 14 | 0.89 | 50 |
| φ30.0 | 31.5±0.70 | 0.45 | 15 | 0.89 | 50 |
| φ35.0 | 36.00±0.70 | 0.5 | 17.5 | 0.89 | 50 |
| φ40.0 | 40.70±0.70 | 0.5 | 20 | 0.89 | 50 |
| φ50.0 | 50.70±0.70 | 0.5 | 25 | 1 | 50 |
ApplicationHeat Shrinkable Tube forms by chemical cross-linked (byradiation) thermally stabilized flame retarded polyolefin. It has excellent un-flammability, flexibility,and insulation.The shrinking temperature is very low and it can shrink very quickly.
It is widely used for various electric insulation and bonding of cales and connectors and applied for connecting end handling of electric wire, insulating and harness of electric wire.