silicone material Higher efficiency. Good transparency. Easily added and dispersed.
silicone material.
Product property:
TSA series high-grade delusterant powder has improves its porosity to 1.8 and decrease the distribution of micropores and ulta-large pores.Besides,the purity of SiO2 in TSA Series reaches 99.3%,and special method is adopted for surface treatment so that its refraction index reaches 1.47, which greatly improves its transparency in coating film and avoid low-grade delusterant powder's problem of turning white and blue on the surface.The delusterant can be easily added in any production procedure and can be easily dispersed.
TSA Series main application:
High-grade furniture coatings
HIgh-grade decorative coatings
Film coating,such as decoration film,man-made or natural leather
Coil coating
Leather
Technical Data
| Item | TSA-220 | TSA-230 | TSA-250 | TSA-260 | TSA-270 | TSA-220L | TSA-230L | TSA-250L | TSA-260L | TSA-270L |
Content of SIO2 (dry basis),% | 99.3 | 99.3 | 99.3 | 99.3 | 99.3 | 99.3 | 99.3 | 99.3 | 99.3 | 99.3 |
| Porosity ml/g | 1.8~2.0 | 1.8~2.0 | 1.8~2.0 | 1.8~2.0 | 1.8~2.0 | 1.8~2.0 | 1.8~2.0 | 1.8~2.0 | 1.8~2.0 | 1.8~2.0 |
| Oil factor g/100g | 280~330 | 270~320 | 260~310 | 250~300 | 250~300 | 280~330 | 270~320 | 260~310 | 250~300 | 250~300 |
| Particle size(Malvent).um | 2~2.5 | 3~3.5 | 4~4.5 | 5~5.5 | 6~7 | 2~2.5 | 3~3.5 | 4~4.5 | 5~5.5 | 6~7 |
| Loss on drying(105°C,2Hrs),%,less | 5 | 5 | 5 | 5 | 5 | 5 | 5 | 5 | 5 | 5 |
| Ignition loss(1000°C,2Hrs),%,less | 7 | 7 | 7 | 7 | 7 | 7 | 7 | 7 | 7 | 7 |
| Specific gravity,g/ml | 2.4 | 2.4 | 2.4 | 2.4 | 2.4 | 2.3 | 2.3 | 2.3 | 2.3 | 2.3 |
| Whiteness | 95 | 95 | 95 | 95 | 95 | 95 | 95 | 95 | 95 | 95 |
| PH(5% liquor) | 7 | 7 | 7 | 7 | 7 | 7 | 7 | 7 | 7 | 7 |
| Surface treatment | Organic | Organic | Organic | Organic | Organic | Organic+Wax | Organic+Wax | Organic+Wax | Organic+Wax | Organic+Wax |
APPlication fields:
1.Furniture coating,Decorative coating recommended:TSA-230,TSA-250,TSA-260,TSA-270,TSA-250L,TSA260L.TSA-270L.
2.Coil coating recommended:TSA-260,TSA-270,TSA-260L,TSA270L.
3.Leader,Leatheroid recommended:TSA-220,TSA-230.
4.Thin film coating recommended:TSA-220.
Experimental data of dispersion of TSA series high-grade Matting Agent
| Item | TSA-220 | TSA-230 | TSA-250 | TSA-260 | TSA-270 | TSA-220L | TSA-230L | TSA-250L | TSA-260L | TSA-270L |
| Dispersion time,mins | 15 | 15 | 15 | 15 | 15 | 15 | 15 | 15 | 15 | 15 |
| Dispersion speed,r/min | 1500 | 1500 | 1500 | 1500 | 1500 | 1500 | 1500 | 1500 | 1500 | 1500 |
| Dispersion fineness,um | 16 | 20 | 23 | 25 | 28 | 16 | 20 | 25 | 28 | 30 |