Reinforced PA6 1.High tensile strength 2.Tough resistance,impact resistance Premium 3.Self-lubrication,wear resistance, chemi
Reinforced PA6
1.Performance
(ITEM) | (UNIT) | (STANDARD) | G10 | G20 | G30 | G30-I | G30-U | G45 |
Tensile Strength | MPa | ISO 527-2 | 105 | 125 | 170 | 150 | 160 | 195 |
Tensile Elongation | % | ISO 527-2 | 3 | 3 | 2 | 3 | 3 | 2 |
Flexural Strength | MPa | ISO 178 | 165 | 200 | 225 | 210 | 220 | 270 |
Flexural Module | MPa | ISO 178 | 4000 | 5500 | 8000 | 7000 | 7800 | 10000 |
Charpy Notch Impact | KJ/m2 | ISO 179-1 | 8.5 | 13 | 17 | 30 | 20 | 21 |
Izod Notch Impact | KJ/m2 | ISO 180 | 8 | 11 | 18 | 32 | 20 | 22 |
Mass Density | g/cm3 | ISO 1183 | 1.2 | 1.28 | 1.37 | 1.36 | 1.37 | 1.53 |
H.D.T | °C | ISO 75 | 190 | 220 | 220 | 215 | 220 | 220 |
Shrinkage For Injection Molding | % | GB/T-15585 | 0.4-0.8 | 0.2-0.6 | 0.2-0.6 | 0.2-0.6 | 0.2-0.6 | 0.2-0.5 |
Characteristics |
|
| General | General | General | Impact resistance
| Hydrolysis
| High rigidity
|
2. Glass fiber reinforced PA6 Nylon glass fiber, the rigidity, heat resistance, aging resistance is obviously improved, creep, water absorption and shrinkage decreases, the surface hardness and wear resistance increase was mainly non-ferrous metals used in place of the engine hood, door Handles and other automobile parts, industrial gear, power tools housing, coil skeleton, railway equipment, fishing gear, electrical and electronic connectors and other fields.
3.Recommended processing conditions:
Drying temperature :80-100 ,3-4HFeeding section: 200 ~ 210 °C the middle section: 250 ~ 290 °C nozzle section: 250 ~ 280 °CInjection pressure of 70 ~ 120MPaHolding pressure 40 ~ 80 MpaMold temperature 70 ~ 100 °CBack pressure 0 ~ 10 Mpa
4.payment: T/T L/C
Package: 25kg/bag
color: as you require
ISO9001:2000
Modified Engineering Plastic Material Reinforced PA6