characteristic of high temperature resistance (300degrees), corrosion resistance, insulation, good mechanical strength
The product has been passed by SGS and INT authorities.
It is widely used in electronic, chemistry, electrical and communication industries.
Shrinkable Temperature ( °C ) | >= 200 | Concentricity (%) | >= 60 |
Radial Shrink Range (%) | >= 45 | Ultimate Elongation Ratio | 300 |
Operate Temperature Range | -80 °C ~280 °C | Coefficient of Dynamic Friction | 0.1 |
Longitudinal Change (%) | <= 10 | Specific Gravity (g/cm 3 ) | 2.16 |
Aging in Circulating-air Oven | 300 °C | Tensile Strength (MPa) | 20.5 |
Aged Tensile Strength Break Elongation | 20 200 | Impact Strength | -No Break -107 |
Volume Resistivity ( Ω. cm) | >10 | Flexural Modulus (MPa) | 400 |
Breakdown Strength (KV/mm) | 30 | Hardness (Shore D) | 85 |
Flammability | VW-1 | Softening Point ( °C ) | 350 |
Operate Temperature ( °C ) | -280~300 | Flammability | VW-1 |
Dissipation Factor | 0.0002 | Weather Resistance | No Break |
Dielectric Constant | 2.1 | Original Volume Resistivity ( Ω. cm) | 1018 |
Arc Resistance | 300 | Solvent Resistance | Excellent |
Chemical Resistance | Excellent |
Size | Before Shrink | After Shrank | |||
I.D. (mm) | Average Layer Thickness (mm) | I.D. (mm) | Average Layer Thickness (mm) | Average Layer Thickness (super thin) (mm) | |
Φ0.5 | 0.5±0.2 | 0.15±0.1 | ≤0.30 | 0.20±0.1 | 0.10±0.05 |
Φ0.8 | 0.8±0.2 | 0.15±0.1 | ≤0.35 | 0.20±0.1 | 0.10±0.05 |
Φ1.0 | 1.0±0.2 | 0.15±0.1 | ≤0.50 | 0.20±0.1 | 0.10±0.05 |
Φ1.5 | 1.5±0.2 | 0.20±0.1 | ≤0.75 | 0.25±0.1 | 0.10±0.05 |
We have the sizes from 0.5~15.
PTFE Heat Shrinkable Tube