Solar Cell Tab Wire, Tab Riboon 1 Well performance 2 Low resistivity 3 Chemical properties stability 4 Well flow performance
The Feature Of Solar Tab Wire: 1. Solar cell tab wire well performance, tin 60% lead 40%, tin 63% lead 37% or tin 62% lead 36% 2% silver solder guarantee that soldering is at low temperature. Unique and excellent solder additives ensure the flow of solder;
2. The superior of the copper-based is with low resistivity, which ensures the solder charged low resistance and does not cause loss of power components;
3. Chemical properties stability, solder is with well flow performance and low temperature performance, whic.h to ensure the appearance of the pattern, smooth and bright, no tin slag, no exposed copper;
4. The automated soldering process ensures solar cell tab wire with the stability and consistency of quality;
5. Common Solar Cell Tab Wire Specification
Size(WxT) | Thickness | Error | ||
Copper Base | Tin | Width | Thickness | |
1.5x0.15 | 0.1 | 0.025 | ±0.1 | ±0.01 |
1.5x0.18 | 0.125 | 0.025 | ±0.1 | ±0.01 |
1.6x0.15 | 0.1 | 0.025 | ±0.1 | ±0.01 |
1.8x0.15 | 0.1 | 0.025 | ±0.1 | ±0.01 |
1.8x0.18 | 0.125 | 0.025 | ±0.1 | ±0.01 |
2.0x0.15 | 0.1 | 0.025 | ±0.1 | ±0.01 |
2.0x0.18 | 0.125 | 0.025 | ±0.1 | ±0.01 |
2.0x0.20 | 0.15 | 0.025 | ±0.1 | ±0.01 |
2.5x0.15 | 0.1 | 0.025 | ±0.1 | ±0.01 |
2.5x0.18 | 0.125 | 0.025 | ±0.1 | ±0.01 |
1.5x0.20 | 0.15 | 0.025 | ±0.1 | ±0.01 |
2.5x0.15 | 0.1 | 0.025 | ±0.1 | ±0.01 |
2.5x0.18 | 0.125 | 0.025 | ±0.1 | ±0.01 |
1.5x0.20 | 0.15 | 0.025 | ±0.1 | ±0.01 |
4.0x0.15 | 0.1 | 0.025 | ±0.1 | ±0.015 |
4.0x0.20 | 0.15 | 0.025 | ±0.1 | ±0.015 |
5.0x0.15 | 0.1 | 0.025 | ±0.1 | ±0.015 |
5.0x0.20 | 0.15 | 0.025 | ±0.1 | ±0.015 |
5.0x0.25 | 0.2 | 0.025 | ±0.1 | ±0.015 |
5.0x0.30 | 0.25 | 0.025 | ±0.1 | ±0.015 |
5.0x0.35 | 0.3 | 0.025 | ±0.1 | ±0.015 |
6.0x0.20 | 0.15 | 0.025 | ±0.1 | ±0.015 |
6.0x0.25 | 0.2 | 0.025 | ±0.1 | ±0.015 |
6.0x0.30 | 0.25 | 0.025 | ±0.1 | ±0.015 |
6.0x0.35 | 0.3 | 0.025 | ±0.1 | ±0.015 |
Solar Cell Tab Wire, Solar Cell Tab Riboon For sale