FR-LSOH insulating compound
Suzhou Mega Plastics Co., Ltd. [China] 
Introduction: Flame-retardant polyolefin low-Smoke non-halogen compound can be uesd for power cable,telecommunication&eletrical
| Test Items | Unit | Typical Value | ||
| MG80012(J) | MG80012(H) | MG80011(G) | ||
| Density | g/cm³ | 1.47 | 1.46 | 1.60 |
| Tensile strength | Mpa | 12.3 | 11.7 | 10.2 |
| Elongation at break | % | 190 | 180 | 100 |
| Air oven again | °C×h | 100×168 | 100×168 | - |
| Tensile strength after again | 13.5 | 12.8 | - | |
| Variability of Tensile strength | % | +10 | +9.4 | - |
| Elongation at break after again | 168 | 155 | - | |
| Variability of Elongation at break | % | -11.5 | -13.9 | - |
| low temperature impact Brittleness | °C | -25 pass | -25 pass | - |
| 20°C Volume resistivity | Ω.cm | 5.1×1014 | 1.5×1013 | - |
| Dielectric strength | MV/m | 28 | 27 | - |
| Oxygen index | % | 34 | 35 | 45 |
| HCI Acid gas emission | mg/g | 0 | 0 | 0 |
| PH | 6.0 | 6.3 | 5.4 | |
| Conductivity | μ s/mm | 0.4 | 0.6 | 1.0 |
| (1.0mm)Smoke density | flame | 48 | 55 | 64 |
| non-flame | 142 | 151 | 168 | |