Polycarboxylate Water reducing and Set retarding Concrete admixture
JK-06 PL is a ready-to-use aqueous solution of hydroxylated organic compounds with water reducing and set retarding Packaging & Delivery
Packaging Detail: | Woven bags with plastic liners. Net weight:25kg+/-0.2kg |
Delivery Detail: | 10-15 Days |
High platicizing effect Substantial water reduction High control of slump loss Improve finish charateristics Chloride free
DescriptionJK-06 PL is a ready-to-use aqueous solution of hydroxylated organic compounds with water reducing and set retarding for concrete. JK-06 PL is a liquid set retarding concrete admixture with a plasticizing effect. Substantial water reduction can be achieved without loss of workability. It complies with ASTM C494 Type D specifications. UsesJK-06 PL is recommended for use in all applications where high quality concrete with superior workability, high temperature, long hauls, ready-mix and extended set time and dense concrete is required. AdvantageExtends concrete initial setting time for proper finishing without cold joint during hot weather.Long-lasting control of slump loss, Reduce water without loss of workability and improved finishing characteristics.Provides decreased permeability but increased durability and strength and reduced shrinkage and creep.Chloride free, does not attack reinforcement. Technical Data SheetItems | Criteria | Test Results (C×0.4%) | ||
Water Reducing Rate (%) | ≥8 | 12.1 | ||
Ratio of Bleeding Rate (%) | ≤100 | 63.7 | ||
Air Content (%) | <5.5 | 4.5 | ||
Setting Time Difference (min) | Initial | >+90 | +172 | |
Compressive Strength Ratio (%) | 7 days | ≥110 | 118 | |
28 days | ≥110 | 117 | ||
Shrinkage (%) | 28 days | ≤135 | 108 | |
Alkali Content (%) | ----- | 0.52 | ||
Alkali Content per m3 (kg) | ≤1.0 | 0.005 | ||
Chloride Ion Content | ----- | 0.15 | ||
Chloride Ion Content per m3(kg) | Prestress Concrete | <0.02 | 0.002 | |
Reinforced Concrete | 0.02~0.20 | |||
Plain Concrete | 0.20~0.60 | |||
Ammonia Content (%) | ≤0.1 | 0.005 | ||
Radiation | Internal Exposure Index, IRa | ≤1.0 | 0.13 | |
External Exposure , Index, IY | ≤1.0 | 0.46 | ||
Polycarboxylate Water reducing and Set retarding Concrete admixture