XIN TAO 99 Support Media(stock)
Detailed Product Description
XINTAO 99 Support Media |
Introduction The XINTAO 99 High Alumina Support Media is equal Denstone 99 Support Media. It is inchemical composition99+% alpha alumina and a maximum 0.2wt% SiO 2 . Because of its highalumina content and low silica (SiO2 ), it's a very excellent and ideal product for high temperature and steam applications, such as secondary reformers in ammonia processing, where leached silica will coat downstream equipment or foul the catalyst bed. The XINTAO 99 High Alumina Support Media has very excellent thermal properties, with its high density high-temperature resistance 1550, also it's a good choice for heat retention or equilibration media. For its superior chemical resistance, it's suitable for applications in olefin processes, such as ethylene dryers, where there's the polymerization problem. Chemical composition Typical Technical Composition | Min. % | Max. % | Usual % | SiO2 | ****** | 0.20 | 0.18 | Al2O3 | 99.00 | 99.60 | 99.30 | Fe2O3 | ****** | 0.20 | 0.02 | TiO2 | ****** | 0.55 | 0.02 | CaO | ****** | 0.10 | 0.20 | MgO | ****** | 0.10 | 0.05 | Na2O | ****** | 0.25 | 0.10 | K2O | ****** | 0.20 | 0.13 |
Physical properties Index | Value | Value | Leachable Iron | ≤ 0.01% | | Apparent Porosity by Weight | ≤ 7.0% | | Moh's Hardness Scale | >8.0 | | Water Absorption | <4.0wt.% | | Acid Resistance | >99.8% | | Thermal Conductivity | 0.7-0.8 w/m 2 .k | | Thermal Expansion @ 500 | 0.10% | | Thermal Shock Stability, 1000 then water cooling | 10 times | | Max. Operating Temperature | 1550 | 2822 | Specific Density | 3,400 kg /m 3 | 212 lb /ft 3 | Bulk Density (Packing Density) | 2,100 g /cm 3 | 131 lb /ft 3 |
Crush Strength Size / | Crush Strength | Nominal Size | (lbs) | (kg) | (N/pc) | mm | inch | min. | min. | min. | 3 | 1/8 | 115 | 52 | 510 | 6 | 1/4 | 230 | 105 | 1030 | 10 | 3/8 | 440 | 200 | 1961 | 13 | 1/2 | 1355 | 615 | 6031 | 16 | 5/8 | 1720 | 780 | 7650 | 19 | 3/4 | 2315 | 1050 | 10297 | 25 | 1 | 3130 | 1420 | 13925 | 38 | 1-1/2 | 4034 | 1830 | 17946 | 50 | 2 | 4960 | 2250 | 22065 |
|