1The scope of application of zirconia ceramic ball Sand mill ,Stirring mill ,Roller mill ,Vibration mill2High-density Highhardne Specifications

Excellent wear resistance,Weight loss of ball lee of ppm, High density, grinding efficiency, No impurity,

Name: JINAO  zirconia beads

Category: yttria zirconia beads Technology: Sintering Size :0.2-60mm Density: 6.0g/cm3 Accumulation of proportion: 3.6g/ml -3.7g/mlHardness: 1250HV1 

Zirconia (YSZ) grinding media is the most durable and efficient media for ball milling and attrition milling of ceramic materials.   Zirconia grinding media provides a virtually contamination-free ball milling solution for a variety of industries.

Advantages of Zirconia Grinding Media:

1)       Ultra low wear loss as a result of the transformation-toughening mechanism unique to the yttrium stabilited zirconia(YST) material system

2)       Higher grinding efficiency and reduced grinding time due to the higher density of zirconia (compared with alumina and glass)

3)       Most durable grinding material, reducing operational cost in the long run. Wear rate substantially lower than Al2O3, CeO2-ZrO2, and MgO-ZrO2 grinding media.

4)       Suitable for high velocity operations and wet grinding operations.

Applications: 1, wear-resistant, corrosion-resistant products: paints, textiles, paints, printing and dyeing 2, high strength, high toughness products: magnetic materials, piezoelectric ceramics, dielectric ceramics 3, to prevent pollution: medicine, food, cosmetics 4, Ceramics: Electronic ceramics, refractory ceramics, structural ceramics  Physical parameters

	Items	unit	parameter
	Compsision	wt%	94.8% ZrO2 5.2% Y2 O3
	Packed Density	Kg/L	3.73(Φ2mm)
	Specific Density	g/cm3	≥6.02
	Hardness(HV)	GPa	>8.5
	Elastic modulus	GPa	200
	Thermal Conductivity	W/m.K	3
	Crushing Load	KN	≥20 (Φ2mm)
	Fracture Toughness	MPam1-2	9
	Grain size	µm	≤0.5
	Thermal expansionCoeffcient(20-400 °C)	10x10 -6 / °C(20-400)	9.6

JINAO yttria stabilized zirconia ceramic ball