Al2O3 Micropowder
Al2O3 Micropowder
Character & Uses
Name | Type | Phase | Character & Uses | |||||
GW-1 | active micropowder | α.Al2O3 transform rate >93% | 1.D50 <1.2 μm; 2. Higher activity; 3. Using GW-1 & GW-2 to make refractory castables which could obtain low water-addition and better flowability; 4. Wihout additives. | |||||
GW-2 | micropowder | α.Al2O3 | 1. 4.0 μm <D50 <4.5 μm; 2. Without additives; 3. Using GW-2 and GW-1 to make refractory castables. | |||||
GW-S1 | double peaks micropowder | α.Al2O4 | 1. D50 approximate 1.0 μm; 2. Containing dispersant 3. Fornmulating corundum or corundun-spinel castables without silicons ashes; 4. Formulating high alumina self-flowing castables with 5-5.5% water-addition and more than 200mm self material and proportion are suitable. 5. Formulating corundum or high bauxite with silicon ashes low water vibration castables the water-addition could reduce to about 4.0%. | |||||
GLW-1 | high alumina micropowder | α.Al2O5 | 1.Al2O3 >85%; 2.Blaine >600 m²/kg; 3. Using with silicon micropowder to formulate low cement castables with high performance and low price. |
Products Quality
Typical techonologic data | GW-1 Active Grade | GW-2 Micropowder | GW-S1 double peaks | GLW-1 high alumina |
Chemical composition | ||||
Al2O3 (%) | 98.70 | 98.76 | 98.66 | ≥86.0 |
SiO2 (%) | 0.12 | 0.12 | 0.12 | <5.5 |
Fe2O3 (%) | 0.12 | 0.12 | 0.12 | <2.0 |
Na2O(%) | 0.30 | 0.28 | 0.30 | 3.43 |
Specific Gravity (g/cm³) | 3.95 | 3.96 | 3.95 | |
Particle Size | ||||
D50 | 0.96 | 4.30 | 0.95 | |
D60 | 3.00 | 18.00 | 3.98 | |
Blaine (m²/kg) | ≥600 |
Al2O3 Micropowder