Carbon Fibre is usually used to modeling, extrusion, blowing mold, spraying smear, moulding in mechanic process and etc.
Carbon Fibre Compound Material (Nylon 66)
It holds the good characteristics as good mechanic tenacity, high tensility resistance, abrasion resistance, self-lubricating, hest resistance, stability, especially grease resistance, which is easy to dissolve in phenol and formyl acid solvent. So, it is usually used to modeling, extrusion, blowing mold, spraying smear, moulding in mechanic process, jointing and conglutinating field.
Technical parameters
Content | 30%CF-42%CF |
Rupture Tensile Strength | 2350Kg/cm2-3250Kg/cm2 |
Rupture Elongation Percentage | 3% |
Break Resistance Strength | 3280Kg/cm2 |
Rigidity | D-85 Shore – D-90 Shore |
Module Contractibility | 0.0003 mm/mm |
Heat Distortion Temperature | 265 |
Proportion | 1.256-1.45 |
Carbon Fibre Compound Material(Nylon 66)