Aluminium Equal Angle 1.Mill finish, anodizing ,powder coating 2.Short lead time of 7 to 15 days 3.Factory direct price
Aluminium Equal Angle1.Mill finish, anodizing ,powder coating 2.Short lead time of 7 to 15 days 3.Factory direct price
We are professional manufacturer for aluminum extrusion, aluminum pipe, aluminum profile
Aluminum extruded products
Material: Aluminium alloy 6063, 6061, 6005, etc.
Temper: T5, T6, etc
6063-T5 aluminum extrusion
T5 temper 6063 has an ultimate tensile strength of at least 22,000 psi (152 MPa) in thicknesses up to 0.5-inch (13 mm), and 21,000 psi (145 MPa) from 0.5 to 1.0-inch (25 mm) thick, and yield strength of at least 16,000 psi (110 MPa) up to 0.5-inch (13 mm) and 15,000 psi (103 MPa) (from 0.5 to 1.0-inch (25 mm). It has elongation of 8%.
6063-T6 aluminum extrusion
T6 temper 6063 has an ultimate tensile strength of at least 30,000 psi (207 MPa) and yield strength of at least 25,000 psi (172 MPa). In thicknesses of 0.124-inch (3.1 mm) or less, it has elongation of 8% or more; in thicker sections, it has elongation of 10%.
6061-T6 aluminum extrusion
T6 temper 6061 has an ultimate tensile strength of at least 42,000 psi (290 MPa) and yield strength of at least 35,000 psi (241 MPa). More typical values are 45,000 psi (310 MPa) and 40,000 psi (275 MPa), respectively.[3] In thicknesses of 0.250 inch (6.35 mm) or less, it has elongation of 8% or more; in thicker sections, it has elongation of 10%. T651 temper has similar mechanical properties. The famous Pioneer plaque was made of this particular alloy. A material data sheet [4] defines the fatigue limit under cyclic load as 14,000 psi.
Surface finish: Mill finish,Anodized,Powder coating,Electrophoresis.
Aluminium Equal Angle